PBT VALOX™ YL-4530
53
- Properties:Glass fiber reinforcedHigh impact resistance
- Usages:Automotive ApplicationsElectrical applications
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 2.1 % | |
| ASTM D955 | 2.0 % | ||
| ISO 294-4 | 2.1 % | ||
| ISO 294-4 | 2.1 % | ||
| Water absorption rate | ASTM D570 | 0.37 % | |
| ISO 62 | 0.50 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 207 Mpa | |
| ISO 527-2/1 | 240 Mpa | ||
| tensile strength | ASTM D638 | 13.9 Mpa | |
| ISO 527-2 | 14.2 Mpa | ||
| elongation | ASTM D638 | 54 % | |
| Tensile strain | ISO 527-2 | 40 % | |
| Flexural modulus | ASTM D790 | 262 Mpa | |
| ISO 178 | 270 Mpa | ||
| ASTM D3702Modified | 0.48 | ||
| ASTM D3702Modified | 0.46 | ||
| Wear factor | ASTM D3702Modified | 5.00 10^-10in^5-min/ft-lb-hr |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/1A | 27 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/1U | NoBreak | |
| Dart impact | ASTM D3763 | 27.7 J | |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 26.9 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ASTM D648 | 47.2 °C | |
| ASTME831 | 1.1E-04 cm/cm/°C | ||
| ISO 11359-2 | 1.1E-04 cm/cm/°C | ||
| ASTME831 | 1.8E-04 cm/cm/°C | ||
| ISO 11359-2 | 1.8E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.