PBT YL-4530 SABIC INNOVATIVE US
VALOX™
Automotive Applications、Electrical applications
Glass fiber reinforced、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/YL-4530 |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 26.9 J | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 27 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 27.7 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/YL-4530 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 240 Mpa | |
| ASTM D638 | 207 Mpa | ||
| elongation | 屈服 | ASTM D638 | 54 % |
| Flexural modulus | ISO 178 | 270 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 40 % |
| Wear factor | Washer | ASTM D3702Modified | 5.00 10^-10in^5-min/ft-lb-hr |
| Dynamic | ASTM D3702Modified | 0.48 | |
| Static | ASTM D3702Modified | 0.46 | |
| tensile strength | 屈服 | ASTM D638 | 13.9 Mpa |
| 屈服 | ISO 527-2 | 14.2 Mpa | |
| Flexural modulus | ASTM D790 | 262 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/YL-4530 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 2.1 % |
| MD：24小时 | ASTM D955 | 2.1 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.37 % |
| 平衡,23°C,50%RH | ISO 62 | 0.50 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 2.0 % |
| TD:24小时 | ISO 294-4 | 2.1 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/YL-4530 |
|---|---|---|---|
| TD：-40到40°C | ISO 11359-2 | 1.8E-04 cm/cm/°C | |
| Hot deformation temperature (HDT) | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 47.2 °C |
| TD：-40到40°C | ASTME831 | 1.8E-04 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C | |
| MD：-40到40°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |