PBT/ASA

PBT/ASA A3 GF 30 Schulman Plastics

Properties:
Low warpage and good surface smoothness
Compare

Technical Data Sheet

other	Test Condition	Test Method	Test Result
Burning wire flammability index	1.50 mm	IEC 60695-2-12	700 ℃
Burning wire flammability index	Burning wire flammability index	3.00 mm	IEC 60695-2-12	750 ℃
Hot filament ignition temperature	1.50 mm	IEC 60695-2-13	725 ℃
Hot filament ignition temperature	Hot filament ignition temperature	3.00 mm	IEC 60695-2-13	775 ℃
Extreme Oxygen Index		ISO 4589-2	20 %
Burning rate	2.00 mm	FMVSS 302	16 mm/min
Flammability level		UL 94	HB
Flammability level	Flammability level		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30℃	ISO 179/1eA	8.0 kJ/m²
	Charpy Notched Impact Strength	23℃	ISO 179/1eA	9.0 kJ/m²
		Charpy Notched Impact Strength	-30℃	ISO 179/1eU	48 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃	ISO 179/1eU	50 kJ/m²
Tensile strain	Break	ISO 527-2/1A/5	2.5 %
Tensile modulus		ISO 527-2/1A/1	9300 MPa
tensile strength	Break	ISO 527-2/1A/5	118 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/Bf	214 ℃
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	180 ℃
Vicat softening temperature	--	ISO 306/A50	210 ℃
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	145 ℃
Ball Pressure Test	200℃	IEC 60695-10-2	Pass

Physical properties	Test Condition	Test Method	Test Result
density	MVR 250°C/2.16 kg	ISO 1183/A	1.42 g/cm³
Melt Volume Flow Rate (MVR)		ISO 1133	20.0 cm³/10min

Electrical performance	Test Method	Test Result
Surface resistivity	IEC 60093	＞1.0E+16 ohm
Volume resistivity	IEC 60093	＞1.0E+14 ohm·cm
Compared to the anti leakage trace index	IEC 60112	PLC 1

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H 358/30	ISO 2039-1	184

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.