Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| GranuleHumidity | | 内部方法 | <0.050 % |
| Water absorption rate | | ASTMD570 | 0.060 % |
| density | | ASTMD792 | 1.48to1.50 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.30to0.50 % |
| Shrinkage rate | | ASTM D955 | 0.40to0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-13 | 750 °C |
| Limiting Oxygen Index | | ASTM D2863 | 24 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 8200 MPa |
| tensile strength | Break | ASTMD638 | 120 MPa |
| elongation | Break | ASTMD638 | 2.8 % |
| Flexural modulus | | ASTMD790 | 7800 MPa |
| bending strength | | ISO 178 | 170 MPa |
| bending strength | Break | ASTM D790 | 170 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 42 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 70 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 34 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/B50 | 226 °C |
| ball-indentation hardness | | VDE0470 | 通过 |
| melting temperature | | ASTMD211 | 252 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 3.5E-05 cm/cm/°C |
| Heat distortion temperature | | ASTMD648 | 230 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.