PBT+PET POCAN® T 7331 000000

0

Technical Data Sheet

physical property Test ConditionTest MethodTest Result
Water absorption rateISO 620.30 %
Water absorption rateISO 620.10 %
Viscosity valueISO 162891.0 ml/g
densityISO 11831.55 g/cm³
Apparent densityISO 600.80 g/cm³
Melt volume flow rateISO 113330.0 cm³/10min
Shrinkage rateISO 294-40.90 %
Shrinkage rateISO 294-40.20 %
Shrinkage rateISO 294-40.30 %
Shrinkage rateISO 294-40.10 %
hardnessTest ConditionTest MethodTest Result
ball-indentation hardnessISO 2039-1200 MPa
flammabilityTest ConditionTest MethodTest Result
Burning BehaviorISO 3795passed
Burning wire flammability indexIEC 60695-2-12750 °C
Limiting Oxygen IndexISO 4589-221 %
UL flame retardant ratingUL 94HB
UL flame retardant ratingUL 94HB
Supplementary InformationTest ConditionTest MethodTest Result
electrolytic corrosionIEC 60426A1
ISO ShortcutISO 7792PBT+PET.GHMR.09-100.GF30
Mechanical propertiesTest ConditionTest MethodTest Result
bending strengthASTM D790207 MPa
bending strengthISO 178230 MPa
Bending Strain3.0 %
Tensile modulusASTM D6389980 MPa
Tensile modulusISO 527-2/110400 MPa
tensile strength ASTM D638123 MPa
tensile strength ISO 527-2/5145 MPa
elongationASTM D6382.5 %
Tensile strainISO 527-2/52.8 %
Tensile creep modulusISO 899-110000 MPa
Tensile creep modulusISO 899-18500 MPa
Flexural modulusASTM D7908550 MPa
Flexural modulusISO 178/A10300 MPa
Impact resistanceTest ConditionTest MethodTest Result
Charpy Notched Impact StrengthISO 179/1eA<10 kJ/m²
Charpy Notched Impact StrengthISO 179/1eA<10 kJ/m²
Impact strength of simply supported beam without notchISO 179/1eU55 kJ/m²
Impact strength of simply supported beam without notchISO 179/1eU65 kJ/m²
Impact strength of cantilever beam gapISO 180/1A<10 kJ/m²
Impact strength of cantilever beam gapISO 180/1A<10 kJ/m²
Impact strength of cantilever beam gapISO 180/1A<10 kJ/m²
Suspended wall beam without notch impact strengthISO 180/1U55 kJ/m²
Suspended wall beam without notch impact strengthISO 180/1U55 kJ/m²
filmTest ConditionTest MethodTest Result
Thin film puncture strengthISO 6603-22.10 J
Thin film puncture strengthISO 6603-2650 N
Electrical performanceTest ConditionTest MethodTest Result
dielectric strengthIEC 60243-127 kV/mm
relative permittivityIEC 602504.00
relative permittivityIEC 602503.80
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 2
Thermal performanceTest ConditionTest MethodTest Result
Heat distortion temperatureISO 75-2/A200 °C
vicatISO 306/B120205 °C
ball-indentation hardnessIEC 60695-10-2Pass
melting temperatureISO 11357-3225to250 °C
Linear coefficient of thermal expansionISO 11359-23E-05 cm/cm/°C
Linear coefficient of thermal expansionISO 11359-29E-05 cm/cm/°C
thermal conductivityISO 83020.27 W/m/K
RTI ElecUL 746140 °C
RTI ImpUL 746125 °C
RTI StrUL 746140 °C
Half IntervalIEC 6021610.2 °C
Half IntervalIEC 6021613.5 °C
Half IntervalIEC 6021610.2 °C
TemperatureIndexIEC 60216155
Heat distortion temperatureISO 75-2/B220 °C
TemperatureIndexIEC 60216140
TemperatureIndexIEC 60216155
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.