PBT+PET POCAN® T 7331 000000 LANXESS GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodLANXESS GERMANY/POCAN® T 7331 000000
Suspended wall beam without notch impact strength-30°CISO 180/1U55 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA<10 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U55 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA<10 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A<10 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU65 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A<10 kJ/m²
-40°CISO 180/1A<10 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU55 kJ/m²
Supplementary InformationTest ConditionTest MethodLANXESS GERMANY/POCAN® T 7331 000000
electrolytic corrosionIEC 60426A1
ISO ShortcutISO 7792PBT+PET.GHMR.09-100.GF30
hardnessTest ConditionTest MethodLANXESS GERMANY/POCAN® T 7331 000000
ball-indentation hardnessISO 2039-1200 MPa
filmTest ConditionTest MethodLANXESS GERMANY/POCAN® T 7331 000000
Thin film puncture strengthISO 6603-2650 N
ISO 6603-22.10 J
Mechanical propertiesTest ConditionTest MethodLANXESS GERMANY/POCAN® T 7331 000000
Tensile strain断裂,23°CISO 527-2/52.8 %
bending strength23°CASTM D790207 MPa
tensile strength 断裂,23°CASTM D638123 MPa
Bending Strain23°C3.0 %
Tensile modulus23°CISO 527-2/110400 MPa
Flexural modulus23°CISO 178/A10300 MPa
tensile strength 断裂,23°CISO 527-2/5145 MPa
Tensile modulus23°CASTM D6389980 MPa
Tensile creep modulus1hrISO 899-110000 MPa
Flexural modulus23°CASTM D7908550 MPa
Tensile creep modulus1000hrISO 899-18500 MPa
bending strength23°CISO 178230 MPa
elongation断裂,23°CASTM D6382.5 %
Electrical performanceTest ConditionTest MethodLANXESS GERMANY/POCAN® T 7331 000000
dielectric strength23°C,1.00mmIEC 60243-127 kV/mm
relative permittivity23°C,1MHzIEC 602503.80
23°C,100HzIEC 602504.00
Compared to the Leakage Tracking Index (CTI)解决方案AIEC 60112PLC 2
flammabilityTest ConditionTest MethodLANXESS GERMANY/POCAN® T 7331 000000
Burning wire flammability index2.0mmIEC 60695-2-12750 °C
Limiting Oxygen IndexISO 4589-221 %
UL flame retardant rating0.8mmUL 94HB
1.6mmUL 94HB
Burning BehaviorISO 3795passed
physical property Test ConditionTest MethodLANXESS GERMANY/POCAN® T 7331 000000
Shrinkage rateTD:120°C,2hr,2.00mm3ISO 294-40.20 %
density23°CISO 11831.55 g/cm³
Shrinkage rateMD:270°C,2.00mm2ISO 294-40.30 %
Apparent densityISO 600.80 g/cm³
Water absorption rate平衡,23°C,50%RHISO 620.10 %
饱和,23°CISO 620.30 %
Shrinkage rateTD:270°C,2.00mm2ISO 294-40.90 %
Viscosity value降低的粘度ISO 162891.0 ml/g
Melt volume flow rate260°C/5.0kgISO 113330.0 cm³/10min
Shrinkage rateMD:120°C,2hr,2.00mm3ISO 294-40.10 %
Thermal performanceTest ConditionTest MethodLANXESS GERMANY/POCAN® T 7331 000000
Half Interval--10IEC 6021610.2 °C
Linear coefficient of thermal expansionMD：23到55°CISO 11359-23E-05 cm/cm/°C
thermal conductivity23°CISO 83020.27 W/m/K
TemperatureIndex抗张强度IEC 60216155
Linear coefficient of thermal expansionTD：23to55°CISO 11359-29E-05 cm/cm/°C
RTI StrUL 746140 °C
TemperatureIndex介电强度IEC 60216155
melting temperatureISO 11357-3225to250 °C
vicatISO 306/B120205 °C
ball-indentation hardness220°CIEC 60695-10-2Pass
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B220 °C
1.8MPa,未退火，HDTISO 75-2/A200 °C
RTI ImpUL 746125 °C
Half Interval--8IEC 6021610.2 °C
--9IEC 6021613.5 °C
RTI ElecUL 746140 °C
TemperatureIndex拉伸冲击强度IEC 60216140