ABS M205FC ELIX POLYMERS SPANISH

Properties:
Glossy
high
good fluidity
food contact compliance
impact resistance
good
biocompatibility
Usages:
Application in medical and nursing fields
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.06 g/cm³
Melt volume flow rate		ISO 1133	20.0 cm³/10min
Shrinkage rate		ISO 294-4	0.50 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.50 %
Shore hardness		ISO 2039-1	106 MPa

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB mm/min
Burning wire flammability index		IEC 60695-2-12	650 ℃

Mechanical properties	Test Condition	Test Method	Test Result
Tensile strain		ISO 527-2/50	2.6 %
Tensile strain	Tensile strain		ISO 527-2/50	＞15 %
elongation at break		ISO 527-2/50	20 %
Flexural modulus		ISO 178	2600 MPa
bending strength		ISO 178	75.0 MPa
Charpy Notched Impact Strength		ISO 179/1eA	7.0 kJ/m²
	Charpy Notched Impact Strength		ISO 179/1eA	16 kJ/m²
		Charpy Notched Impact Strength		ISO 179/1eU	100 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eU	120 kJ/m²
Impact strength of cantilever beam gap		ISO 180/1A	7.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/1A	15 kJ/m²
Tensile modulus		ISO 527-2/1	2550 MPa
tensile strength		ISO 527-2/50	50.5 MPa
tensile strength	tensile strength		ISO 527-2/50	36.5

Electrical performance	Test Condition	Test Method	Test Result
Dissipation Factor		IEC 60250	0.0053
Dissipation Factor	Dissipation Factor		IEC 60250	0.0096
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 0
Surface Resistivity		IEC 60093	2E+17 ohm
Volume resistivity		IEC 60093	2E+16 ohm·cm
relative permittivity		IEC 60250	2.82
relative permittivity	relative permittivity		IEC 60250	3.04

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/B	98.0 ℃
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	94.0 ℃
vicat		ISO 306/B50	98.0 ℃
vicat	vicat		ISO 306/B120	101 ℃
Linear coefficient of thermal expansion		ISO 11359-2	0.000078 cm/cm/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	0.000081

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.