ABS M205FC ELIX POLYMERS SPANISH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Electrical performance | Test Condition | Test Method | ELIX POLYMERS SPANISH/M205FC |
---|---|---|---|
Dissipation Factor | 23℃, 1 MHz | IEC 60250 | 0.0096 |
Surface Resistivity | IEC 60093 | 2E+17 ohm | |
Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | PLC 0 |
Volume resistivity | IEC 60093 | 2E+16 ohm·cm | |
relative permittivity | 23℃, 1 MHz | IEC 60250 | 2.82 |
Dissipation Factor | 23℃, 100 Hz | IEC 60250 | 0.0053 |
relative permittivity | 23℃, 100 Hz | IEC 60250 | 3.04 |
Mechanical properties | Test Condition | Test Method | ELIX POLYMERS SPANISH/M205FC |
---|---|---|---|
bending strength | 23℃ | ISO 178 | 75.0 MPa |
Charpy Notched Impact Strength | -30℃ | ISO 179/1eA | 7.0 kJ/m² |
Flexural modulus | 23℃ | ISO 178 | 2600 MPa |
tensile strength | 断裂, 23℃ | ISO 527-2/50 | 36.5 |
elongation at break | 23℃ | ISO 527-2/50 | 20 % |
Charpy Notched Impact Strength | 23℃ | ISO 179/1eU | 120 kJ/m² |
Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 15 kJ/m² |
tensile strength | 屈服, 23℃ | ISO 527-2/50 | 50.5 MPa |
Tensile modulus | 23℃ | ISO 527-2/1 | 2550 MPa |
Tensile strain | 屈服, 23℃ | ISO 527-2/50 | 2.6 % |
Charpy Notched Impact Strength | -30℃ | ISO 179/1eU | 100 kJ/m² |
Impact strength of cantilever beam gap | -30℃ | ISO 180/1A | 7.0 kJ/m² |
Tensile strain | 断裂,23℃ | ISO 527-2/50 | >15 % |
Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 16 kJ/m² |
flammability | Test Condition | Test Method | ELIX POLYMERS SPANISH/M205FC |
---|---|---|---|
UL flame retardant rating | 1.60 mm | UL 94 | HB mm/min |
Burning wire flammability index | 2.00 mm | IEC 60695-2-12 | 650 ℃ |
physical property | Test Condition | Test Method | ELIX POLYMERS SPANISH/M205FC |
---|---|---|---|
Melt volume flow rate | 220℃/10.0 kg | ISO 1133 | 20.0 cm³/10min |
Shrinkage rate | TD | ISO 294-4 | 0.50 % |
MD | ISO 294-4 | 0.50 % | |
Shore hardness | 球压硬度 | ISO 2039-1 | 106 MPa |
density | ISO 1183 | 1.06 g/cm³ |
Thermal performance | Test Condition | Test Method | ELIX POLYMERS SPANISH/M205FC |
---|---|---|---|
Linear coefficient of thermal expansion | 23 到 55℃ | ISO 11359-2 | 0.000078 cm/cm/℃ |
Heat distortion temperature | 0.45 MPa, 未退火,HDT | ISO 75-2/B | 98.0 ℃ |
vicat | ISO 306/B50 | 98.0 ℃ | |
Heat distortion temperature | 1.8 MPa, 未退火,HDT | ISO 75-2/A | 94.0 ℃ |
vicat | ISO 306/B120 | 101 ℃ | |
Linear coefficient of thermal expansion | 23 到 55℃,横向 | ISO 11359-2 | 0.000081 |