Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | BS2782620A | 1.50 g/cm³ |
| melt mass-flow rate | | 内部方法 | 14 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore A | | 90 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ISO4589-2 | 31 % |
| Smoke- | | EN61034 | pass |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| HalogenAcidGasEvolution | | IEC60754-2 | <0.50 % |
| tear strength | | BS6469 | 5 N/mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | IEC60811-1-1 | 13.0 MPa |
| Tensile strain | Break | IEC60811-1-1 | 140 % |
| Tensile strain | | IEC60811-1-4 | 50 % |
| aging | Test Condition | Test Method | Test Result |
|---|
| Change rate of tensile strength | | | 17 % |
| Change rate of tensile strength | | | 45 % |
| Change rate of tensile strength | | | 18 % |
| Change rate of tensile strength | | IEC60811-1-2 | 12 % |
| Changes in tensile stress during fracture | | | 14 % |
| Changes in tensile stress during fracture | | | 20 % |
| Changes in tensile stress during fracture | | | 7.0 % |
| Changes in tensile stress during fracture | | IEC60811-1-2 | -10 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60250 | 4.65 |
| InsulationConstant-Ki | | IEC60502 | 9.5E+10 ohms·cm |
| InsulationConstant-Ki | | IEC60502 | 6.5E+07 ohms·cm |
| Volume resistivity | | IEC60502 | 2E+14 ohms·cm |
| dielectric strength | | IEC60243-1 | 19 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| deformation | | IEC60811-3-1 | 15 % |
| cold shock | | IEC60811-1-4 | pass |
| Cold bend | | IEC60811-1-4 | pass |
| | ISO4589-3 | 270 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.