PE AEI TP519C UK AEI Compounds
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UK AEI Compounds/AEI TP519C |
|---|---|---|---|
| Shore hardness | 邵氏A | 90 |
| Supplementary Information | Test Condition | Test Method | UK AEI Compounds/AEI TP519C |
|---|---|---|---|
| tear strength | BS6469 | 5 N/mm | |
| HalogenAcidGasEvolution | IEC 60754-2 | <0.50 % |
| Mechanical properties | Test Condition | Test Method | UK AEI Compounds/AEI TP519C |
|---|---|---|---|
| tensile strength | IEC 60811-1-1 | 13.0 MPa | |
| Tensile strain | 断裂 | IEC 60811-1-1 | 140 % |
| 断裂,-30°C2 | IEC 60811-1-4 | 50 % |
| Electrical performance | Test Condition | Test Method | UK AEI Compounds/AEI TP519C |
|---|---|---|---|
| dielectric constant | 20°C，Ki | IEC 60502 | 9.5E+10 ohms·cm |
| Volume resistivity | 20°C | IEC 60502 | 2E+14 ohms·cm |
| dielectric constant | 90°C，Ki | IEC 60502 | 6.5E+07 ohms·cm |
| relative permittivity | 23°C,50Hz | IEC 60250 | 4.65 |
| dielectric strength | 20°C | IEC 60243-1 | 19 kV/mm |
| flammability | Test Condition | Test Method | UK AEI Compounds/AEI TP519C |
|---|---|---|---|
| smoke | EN61034 | pass | |
| Limiting Oxygen Index | ISO 4589-2 | 31 % |
| physical property | Test Condition | Test Method | UK AEI Compounds/AEI TP519C |
|---|---|---|---|
| density | BS2782620A | 1.50 g/cm³ | |
| melt mass-flow rate | 150°C/21.6kg | 内部方法 | 14 g/10min |
| aging | Test Condition | Test Method | UK AEI Compounds/AEI TP519C |
|---|---|---|---|
| Tensile stress change rate | 70°C,4hr,在ASTM#2油中，断裂 | 7.0 % | |
| 50°C,336hr,inSodiumHydroxide,1N，断裂 | 20 % | ||
| Change rate of tensile strength in air | 135°C,168hr | IEC 60811-1-2 | 12 % |
| Tensile stress change rate | 135°C,168hr，断裂 | IEC 60811-1-2 | -10 % |
| Change rate of tensile strength in air | 70°C,4hr,在ASTM#2油中 | 18 % | |
| Tensile stress change rate | 50°C,336hr,inHydrochloricAcid,1N，断裂 | 14 % | |
| Change rate of tensile strength in air | 50°C,336hr,inHydrochloricAcid,1N | 17 % | |
| 50°C,336hr,inSodiumHydroxide,1N | 45 % |
| Thermal performance | Test Condition | Test Method | UK AEI Compounds/AEI TP519C |
|---|---|---|---|
| cold shock | -30°C | IEC 60811-1-4 | pass |
| deformation | 80°C | IEC 60811-3-1 | 15 % |
| TEMPERATURE | ISO 4589-3 | 270 °C | |
| Cold bend | -30°C | IEC 60811-1-4 | pass |