PA6 Ultramid® B3WG6 BK00564
35
- Properties:Thermal stabilityOil resistantFiller: Glass fiber reinf30%Filler by weight30% filler by weight
- Usages:Automotive sectorEngine hood partsApplication in the automotive field
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTMD792 | 1.36 g/cm³ | |
| ISO1183 | 1.36 g/cm³ | ||
| Melt volume flow rate | ISO1133 | 40.0 cm3/10min | |
| Shrinkage rate | 0.30 % | ||
| Water absorption rate | ASTMD570 | 6.6 % | |
| ISO62 | 6.6 % | ||
| ASTMD570 | 2.1 % | ||
| ISO62 | 2.1 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO527-2 | 9500 Mpa | |
| tensile strength | ASTMD638 | 180 Mpa | |
| Tensile stress | ISO527-2 | 180 Mpa | |
| Tensile strain | ISO527-2 | 3.0 % | |
| Flexural modulus | ISO178 | 8300 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179 | 9.0 kJ/m² | |
| ISO179 | 12 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO179 | 65 kJ/m² | |
| ISO179 | 80 kJ/m² | ||
| Impact strength of cantilever beam gap | ASTMD256 | 110 J/m | |
| ASTMD256 | 150 J/m | ||
| ISO180 | 12 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD648 | 220 °C | ||
| ISO75-2/B | 220 °C | ||
| ASTMD648 | 210 °C | ||
| ISO75-2/A | 205 °C | ||
| ASTMD3418 | 220 °C | ||
| ISO3146 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.