Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 B3WG6 BK00564 BASF SHANGHAI
Ultramid®
Automotive sector、Engine hood parts、Application in the automo
Thermal stability、Oil resistant、Filler: Glass fiber reinf、30%、Filler by weight、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF SHANGHAI/B3WG6 BK00564 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 150 J/m |
| Charpy Notched Impact Strength | -30°C | ISO179 | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 80 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180 | 12 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179 | 65 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ASTMD256 | 110 J/m |
| Charpy Notched Impact Strength | 23°C | ISO179 | 12 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF SHANGHAI/B3WG6 BK00564 |
|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 9500 Mpa |
| Flexural modulus | 23°C | ISO178 | 8300 Mpa |
| tensile strength | 断裂,23°C | ASTMD638 | 180 Mpa |
| Tensile strain | 断裂,23°C | ISO527-2 | 3.0 % |
| Tensile stress | 断裂,23°C | ISO527-2 | 180 Mpa |
| physical property | Test Condition | Test Method | BASF SHANGHAI/B3WG6 BK00564 |
|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.30 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 2.1 % |
| 饱和,23°C | ISO62 | 6.6 % | |
| density | ASTMD792 | 1.36 g/cm³ | |
| Melt volume flow rate | 275°C/5.0kg | ISO1133 | 40.0 cm3/10min |
| density | ISO1183 | 1.36 g/cm³ | |
| Water absorption rate | 饱和 | ASTMD570 | 6.6 % |
| 平衡,50%RH | ASTMD570 | 2.1 % |
| Thermal performance | Test Condition | Test Method | BASF SHANGHAI/B3WG6 BK00564 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 220 °C |
| Melting temperature (DSC) | ISO3146 | 220 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 205 °C |
| 1.8MPa,未退火 | ASTMD648 | 210 °C | |
| 0.45MPa,未退火 | ASTMD648 | 220 °C | |
| Peak Melting Temperature | ASTMD3418 | 220 °C |