PC LNP™ LUBRICOMP™ DFL36EU compound
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ASTM D570 | 0.080 % | |
| ISO 62 | 0.11 % | ||
| density | ASTM D792 | 1.56 g/cm³ | |
| ASTM D792 | 1.56 g/cm³ | ||
| Shrinkage rate | ASTM D955 | 0.10to0.30 % | |
| ASTM D955 | 0.50to0.70 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 9230 MPa | |
| ISO 527-2/1 | 8690 MPa | ||
| tensile strength | Break | ASTM D638 | 116 MPa |
| Break | ISO 527-2/5 | 113 MPa | |
| elongation | Break | ASTM D638 | 2.7 % |
| Tensile strain | Break | ISO 527-2/5 | 2.6 % |
| Flexural modulus | ASTM D790 | 8910 MPa | |
| ISO 178 | 8340 MPa | ||
| Wear factor | ASTM D3702Modified | 30.0 10^-10in^5-min/ft-lb-hr | |
| bending strength | ISO 178 | 175 MPa | |
| ASTM D790 | 190 MPa | ||
| ASTM D790 | 189 MPa | ||
| coefficient of friction | ASTM D3702Modified | 0.47 | |
| ASTM D3702Modified | 0.51 | ||
| Wear factor | ASTM D3702Modified | 2.00 10^-10in^5-min/ft-lb-hr |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 5.30 J | |
| Suspended wall beam without notch impact strength | ISO 180/1U | 51 kJ/m² | |
| Dart impact | ASTM D3763 | 16.9 J | |
| Impact strength of cantilever beam gap | ASTM D256 | 170 J/m | |
| ISO 180/1A | 16 kJ/m² | ||
| ASTM D4812 | 710 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTM D696 | 5.4E-05 cm/cm/°C | |
| ASTM D696 | 4.3E-05 cm/cm/°C | ||
| Heat distortion temperature | ASTM D648 | 146 °C | |
| ISO 75-2/Bf | 145 °C | ||
| ASTM D648 | 141 °C | ||
| ISO 75-2/Af | 141 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.