Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LNP™ LUBRICOMP™ DFL36EU compound SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/LNP™ LUBRICOMP™ DFL36EU compound |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 51 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 16.9 J |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 170 J/m |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 5.30 J | |
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 710 J/m |
| 23°C | ISO 180/1A | 16 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC/LNP™ LUBRICOMP™ DFL36EU compound |
|---|---|---|---|
| Wear factor | Washer | ASTM D3702Modified | 30.0 10^-10in^5-min/ft-lb-hr |
| Flexural modulus | ISO 178 | 8340 MPa | |
| bending strength | ISO 178 | 175 MPa | |
| elongation | 断裂 | ASTM D638 | 2.7 % |
| tensile strength | 断裂 | ISO 527-2/5 | 113 MPa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 190 MPa |
| coefficient of friction | Static | ASTM D3702Modified | 0.51 |
| Tensile modulus | ASTM D638 | 9230 MPa | |
| tensile strength | 断裂 | ASTM D638 | 116 MPa |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.6 % |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 8910 MPa |
| Wear factor | Ring | ASTM D3702Modified | 2.00 10^-10in^5-min/ft-lb-hr |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.47 |
| Tensile modulus | ISO 527-2/1 | 8690 MPa | |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 189 MPa |
| physical property | Test Condition | Test Method | SABIC/LNP™ LUBRICOMP™ DFL36EU compound |
|---|---|---|---|
| Shrinkage rate | MD：24小时 | ASTM D955 | 0.10to0.30 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.080 % |
| 平衡,23°C,50%RH | ISO 62 | 0.11 % | |
| density | ASTM D792 | 1.56 g/cm³ | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.50to0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC/LNP™ LUBRICOMP™ DFL36EU compound |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 145 °C |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 5.4E-05 cm/cm/°C |
| TD：-30to30°C | ASTM D696 | 4.3E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 146 °C |
| 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 141 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 141 °C |