Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | 内部方法 | 3.5 g/10min |
| Water absorption rate | | IEC 60811 | <4.00 mg/cm² |
| Environmental stress cracking resistance | | ASTM D1693 | >1000 hr |
| density | | ASTM D792 | 1.40 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 38 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Discharge of halogenated acids | | IEC 60754-1 | <0.10 % |
| Potential heat energy - high level (total value) | | ISO 1716 | 18.6 MJ/kg |
| Temperature index (combustion) | | NES715 | 300 °C |
| Corrosion of flue gas | | IEC 60754-2 | >4.30 |
| Corrosion of flue gas | | IEC 60754-2 | <10.0 µS/mm |
| Limiting Oxygen Index | | ASTM D2863 | 38 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | IEC 60811 | 12.3 MPa |
| elongation | Break | IEC 60811 | 210 % |
| aging | Test Condition | Test Method | Test Result |
|---|
| Changes in mechanical properties after hot air aging test | | IEC 60811 | 10 % |
| Changes in mechanical properties after hot air aging test | | IEC 60811 | -5 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60502 | 6.7E+14 ohms·cm |
| Volume resistivity | | IEC 60502 | 5.4E+13 ohms·cm |
| dielectric constant | | IEC 60502 | 2500 Mohms·km |
| dielectric constant | | IEC 60502 | 200 Mohms·km |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermosetting | | IEC 60811 | 50 % |
| Hot air contraction | | IEC 60811 | <4.0 % |
| Hot pressing test - maximum permeability, K | | IEC 60811 | <50 % |
| Flexural modulus | | IEC 60811 | 无开裂 |
| impact test | | IEC 60811 | 无开裂 |
| thermosetting | | IEC 60811 | 0.0 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.