PA66 SLOVAMID® 66 GB 20 LS

Compare

Technical Data Sheet

physical property	Test Method	Test Result
Shrinkage rate	STM640808	1.6 %
water content	ISO 960	0.15 %
density	ISO 1183	1.24 g/cm³
melt mass-flow rate	ISO 1133	3.0 g/10min
Shrinkage rate	STM640808	1.7 %

flammability	Test Condition	Test Method	Test Result
Hot filament ignition temperature		IEC 60695-2-13	650 °C
UL flame retardant rating		UL 94	HB

Mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	65.0 MPa
Tensile modulus		ISO 527-2	3100 MPa
tensile strength	Yield	ISO 527-2	45.0 MPa
Tensile strain	Yield	ISO 527-2	20 %
Flexural modulus		ISO 178	2500 MPa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179	1.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179	2.0 kJ/m²
Impact strength of simply supported beam without notch		ISO 179	40 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179	40 kJ/m²

Thermal performance	Test Method	Test Result
Heat distortion temperature	ISO 75-2/B	250 °C
vicat	ISO 306/B	250 °C
melting temperature	ISO 3146	260 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.