Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 SLOVAMID® 66 GB 20 LS PLASTCOM SLOVAKIA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | PLASTCOM SLOVAKIA/SLOVAMID® 66 GB 20 LS |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | -20°C | ISO 179 | 40 kJ/m² |
| Charpy Notched Impact Strength | -20°C | ISO 179 | 1.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | PLASTCOM SLOVAKIA/SLOVAMID® 66 GB 20 LS |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3100 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 20 % |
| tensile strength | 屈服 | ISO 527-2 | 45.0 MPa |
| Flexural modulus | ISO 178 | 2500 MPa | |
| bending strength | ISO 178 | 65.0 MPa |
| flammability | Test Condition | Test Method | PLASTCOM SLOVAKIA/SLOVAMID® 66 GB 20 LS |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 650 °C | |
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | PLASTCOM SLOVAKIA/SLOVAMID® 66 GB 20 LS |
|---|---|---|---|
| Shrinkage rate | MD | STM640808 | 1.6 % |
| density | ISO 1183 | 1.24 g/cm³ | |
| water content | ISO 960 | 0.15 % | |
| melt mass-flow rate | 275°C/0.325kg | ISO 1133 | 3.0 g/10min |
| Shrinkage rate | TD | STM640808 | 1.7 % |
| Thermal performance | Test Condition | Test Method | PLASTCOM SLOVAKIA/SLOVAMID® 66 GB 20 LS |
|---|---|---|---|
| vicat | ISO 306/B | 250 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 250 °C |
| melting temperature | ISO 3146 | 260 °C |