PA6

PA6 SLOVAMID® 6 NG1 GF 20 HLS PLASTCOM SLOVAKIA

Properties:
Filler glass fiber reinforced material 20% filler by weight
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-20°C	ISO 179	7.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	53 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-20°C	ISO 179	48 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	8.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	7600 MPa
bending strength		ISO 178	192 MPa
Bending modulus		ISO 178	6200 MPa
Tensile strain	Yield	ISO 527-2	3.0 %
tensile strength	Yield	ISO 527-2	150 MPa

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 3146	225 °C
Vicat softening temperature		ISO 306/B	202 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	214 °C

Physical properties	Test Condition	Test Method	Test Result
water content		ISO 960	0.15 %
Shrinkage rate	MD	STM640808	0.30 %
Shrinkage rate	Shrinkage rate	TD	STM640808	0.53 %
melt mass-flow rate	230°C/2.16kg	ISO 1133	5.0 g/10min
density		ISO 1183	1.28 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.