Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO 1133 | 54.5 cm³/10min |
| Shrinkage rate | | ASTM D955 | 0.40to0.70 % |
| density | | ISO 1183 | 1.16 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 59 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO 2039-2 | 101 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | 5VA |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2/50 | 44.1 MPa |
| Flexural modulus | | ISO 178 | 2550 MPa |
| bending strength | | ISO 178 | 69.8 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 6.6 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 74.0 °C |
| ball-indentation hardness | | EMAC | 80 °C |
| vicat | | ISO 306/B | 88.0 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 7.0E-5到1.0E-4 cm/cm/°C |
| RTI Elec | | UL 746 | 50.0 °C |
| RTI Imp | | UL 746 | 50.0 °C |
| RTI | | UL 746 | 50.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.