ACS Stylac™ NF920 ASAHI JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/Stylac™ NF920 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 6.6 kJ/m² |
| hardness | Test Condition | Test Method | ASAHI JAPAN/Stylac™ NF920 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 101 |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/Stylac™ NF920 |
|---|---|---|---|
| Flexural modulus | ISO 178 | 2550 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 44.1 MPa |
| bending strength | ISO 178 | 69.8 MPa |
| flammability | Test Condition | Test Method | ASAHI JAPAN/Stylac™ NF920 |
|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL 94 | 5VA |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | ASAHI JAPAN/Stylac™ NF920 |
|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 54.5 cm³/10min |
| density | 23°C | ISO 1183 | 1.16 g/cm³ |
| Shrinkage rate | MD | ASTM D955 | 0.40to0.70 % |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 59 g/10min |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/Stylac™ NF920 |
|---|---|---|---|
| vicat | ISO 306/B | 88.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 74.0 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 7.0E-5到1.0E-4 cm/cm/°C |
| RTI Imp | UL 746 | 50.0 °C | |
| RTI | UL 746 | 50.0 °C | |
| ball-indentation hardness | EMAC | 80 °C | |
| RTI Elec | UL 746 | 50.0 °C |