Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 11 g/10 min |
| Shrinkage rate - flow | | ASTM D955 | 0.40 到 0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 118 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2650 Mpa |
| tensile strength | | ASTM D638 | 59.0 Mpa |
| elongation | | ASTM D638 | > 15 % |
| Flexural modulus | | ASTM D790 | 2850 Mpa |
| bending strength | | ASTM D790 | 96.0 Mpa |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 到 90 °C |
| drying time | | | 3.0 到 4.0 hr |
| Temperature at the rear of the barrel | | | 180 到 200 °C |
| Temperature in the middle of the barrel | | | 190 到 210 °C |
| Temperature at the front of the material cylinder | | | 200 到 220 °C |
| Spray nozzle temperature | | | 200 到 230 °C |
| Processing (melt) temperature | | | 200 到 230 °C |
| Temperature | | | 40 到 60 °C |
| Back pressure 8 | | | 2.94 到 5.88 Mpa |
| screw speed | | | 30 到 60 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648 | 84.0 °C |
| vicat | | ASTM D15257 | 92.0 °C |
| RTI Elec | | UL 746 | 50.0 °C |
| RTI Imp | | UL 746 | 50.0 °C |
| RTI | | UL 746 | 50.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.