ABS XG569C LG CHEM KOREA
--
Electrical enclosure、Electronic field、Electrical field
High gloss、scratch resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodLG CHEM KOREA/XG569C
Rockwell hardnessR 级, 23°C, 注塑ASTM D785118
Mechanical propertiesTest ConditionTest MethodLG CHEM KOREA/XG569C
bending strength23°C, 3.20 mm, 注塑ASTM D79096.0 Mpa
tensile strength屈服, 23°C, 3.20 mm, 注塑ASTM D63859.0 Mpa
Tensile modulus23°C, 3.20 mm, 注塑ASTM D6382650 Mpa
Flexural modulus23°C, 3.20 mm, 注塑ASTM D7902850 Mpa
elongation断裂, 23°C, 3.20 mm, 注塑ASTM D638> 15 %
flammabilityTest ConditionTest MethodLG CHEM KOREA/XG569C
UL flame retardant rating3.0 mmUL 94HB
1.5 mmUL 94HB
physical property Test ConditionTest MethodLG CHEM KOREA/XG569C
melt mass-flow rate220°C/10.0 kgASTM D123811 g/10 min
Shrinkage rate - flow23°C, 3.20 mm, 注塑ASTM D9550.40 到 0.70 %
Thermal performanceTest ConditionTest MethodLG CHEM KOREA/XG569C
RTI ImpUL 74650.0 °C
Thermal deformation temperature under load1.8 MPa, 未退火, 6.40 mm, 注塑ASTM D64884.0 °C
RTIUL 74650.0 °C
vicatASTM D1525792.0 °C
RTI ElecUL 74650.0 °C
injectionTest ConditionTest MethodLG CHEM KOREA/XG569C
Temperature40 到 60 °C
screw speed30 到 60 rpm
Temperature at the rear of the barrel180 到 200 °C
Processing (melt) temperature200 到 230 °C
drying temperature80 到 90 °C
Back pressure 82.94 到 5.88 Mpa
Temperature at the front of the material cylinder200 到 220 °C
drying time3.0 到 4.0 hr
Spray nozzle temperature200 到 230 °C
Temperature in the middle of the barrel190 到 210 °C