Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | 内部方法 | 1.20 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 10 g/10min |
| Shrinkage rate | | ASTM D955 | 1.5to2.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 78 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 12 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 15 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 7.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2 | 55.0 MPa |
| tensile strength | Break | ISO 527-2 | 45.0 MPa |
| Tensile strain | Break | ISO 527-2 | 15 % |
| Flexural modulus | | ISO 178 | 2700 MPa |
| bending strength | | ISO 178 | 89.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | 内部方法 | 1E+03 ohms |
| Volume resistivity | | 内部方法 | 1E+02 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 66.0 °C |
| vicat | | ISO 306/A | 215 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare