PA6 CA3178 Cabot Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Cabot Corporation/ CA3178 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 12 kJ/m² |
| -30°C | ISO 179 | 7.0 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 15 kJ/m² |
| hardness | Test Condition | Test Method | Cabot Corporation/ CA3178 |
|---|---|---|---|
| Shore hardness | 邵氏D,15秒 | ASTM D2240 | 78 |
| Electrical performance | Test Condition | Test Method | Cabot Corporation/ CA3178 |
|---|---|---|---|
| Surface Resistivity | 内部方法 | 1E+03 ohms | |
| Volume resistivity | 内部方法 | 1E+02 ohms·cm |
| Mechanical properties | Test Condition | Test Method | Cabot Corporation/ CA3178 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 45.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 15 % |
| tensile strength | 屈服 | ISO 527-2 | 55.0 MPa |
| Flexural modulus | ISO 178 | 2700 MPa | |
| bending strength | ISO 178 | 89.0 MPa |
| flammability | Test Condition | Test Method | Cabot Corporation/ CA3178 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Cabot Corporation/ CA3178 |
|---|---|---|---|
| melt mass-flow rate | 275°C/10.0kg | ISO 1133 | 10 g/10min |
| Shrinkage rate | MD | ASTM D955 | 1.5to2.0 % |
| density | 23°C | 内部方法 | 1.20 g/cm³ |
| Thermal performance | Test Condition | Test Method | Cabot Corporation/ CA3178 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 66.0 °C |
| vicat | ISO 306/A | 215 °C |