Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | | 0.70 g/cm³ |
| Molten Volume Flow Rate (MVR) | | ISO 1133 | 45.0 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| Water absorption rate | | ISO 62 | 4.3 到 5.3 % |
| Water absorption rate | | ISO 62 | 1.4 到 1.8 % |
| viscosity number | | ISO 307 | 120 cm³/g |
| Mold Shrinkage - Model Heating | | | 0.10 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 50 % |
| Polymer Abbreviation | | | PA6T/6-GF30 FR |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 11000 Mpa |
| Tensile stress | | ISO 527-2 | 150 Mpa |
| Tensile strain | | ISO 527-2 | 2.5 % |
| Flexural modulus | | ISO 178 | 11000 Mpa |
| Bending stress | | ISO 178 | 240 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 65 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 65 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| Volume resistivity | | IEC 60093 | 1.0E+17 ohms·cm |
| | IEC 60250 | 3.90 |
| Dissipation Factor | | IEC 60250 | 0.015 |
| CTI | | IEC 60112 | 600 V |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 110 °C |
| drying time | | | 8.0 hr |
| Suggested maximum moisture content | | | 0.030 % |
| Hopper temperature | | | 80 °C |
| Temperature at the rear of the barrel | | | 300 °C |
| Temperature in the middle of the barrel | | | 310 °C |
| Temperature at the front of the material cylinder | | | 320 °C |
| Spray nozzle temperature | | | 320 °C |
| Processing (melt) temperature | | | 310 到 330 °C |
| Temperature | | | 80 到 120 °C |
| Residence Time | | | < 5.0 min |
| Screw Speed | | | < 18 m/min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/A | 220 °C |
| melting temperature | | ISO 11357-3 | 290 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.