Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.42 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 34 g/10min |
| Shrinkage rate | | 内部方法 | 1.7to2.1 % |
| Water absorption rate | | ASTM D570 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 94 |
| Rockwell hardness | R-Scale | ASTM D785 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTMD638 | 20 % |
| Flexural modulus | | ASTMD790 | 3200 MPa |
| bending strength | | ASTM D790 | 111 MPa |
| Taber abraser | | ASTM D1044 | 13.0 mg |
| Tensile modulus | | ISO 527-2 | 3400 MPa |
| yield | | ISO 527-2 | 73.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 6.0 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 56 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | | 0.23 W/m/K |
| Linear coefficient of thermal expansion | | ASTMD696 | 1E-04 cm/cm/°C |
| specific heat | | | 1470 J/kg/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.