POM Homopolymer Tenac™ 7050 ASAHI JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/Tenac™ 7050 |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 6.0 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 56 J/m |
| hardness | Test Condition | Test Method | ASAHI JAPAN/Tenac™ 7050 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 94 |
| R级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/Tenac™ 7050 |
|---|---|---|---|
| Taber abraser | ASTM D1044 | 13.0 mg | |
| Flexural modulus | ASTMD790 | 3200 MPa | |
| elongation | 断裂 | ASTMD638 | 20 % |
| Tensile modulus | ISO 527-2 | 3400 MPa | |
| yield | ISO 527-2 | 73.0 MPa | |
| bending strength | ASTM D790 | 111 MPa |
| flammability | Test Condition | Test Method | ASAHI JAPAN/Tenac™ 7050 |
|---|---|---|---|
| UL flame retardant rating | 0.750mm | UL 94 | HB |
| 1.50mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ASAHI JAPAN/Tenac™ 7050 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.7to2.1 % |
| density | ASTMD792 | 1.42 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 34 g/10min |
| Water absorption rate | 23°C,24hr,50%RH | ASTM D570 | 0.20 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/Tenac™ 7050 |
|---|---|---|---|
| thermal conductivity | 0.23 W/m/K | ||
| specific heat | 1470 J/kg/°C | ||
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1E-04 cm/cm/°C |