PC LNP™ THERMOCOMP™ D452 compound
0
- Properties:Fillersglass fiber reinforced materials
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.10to0.25 % | |
| ASTM D955 | 0.10to0.25 % | ||
| density | ASTM D792 | 1.52 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 17 g/10min | |
| ASTM D1238 | 39 g/10min | ||
| Melt volume flow rate | ISO 1133 | 12.0 cm³/10min | |
| ISO 1133 | 30.0 cm³/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 13 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 41 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 150 J/m | |
| Suspended wall beam without notch impact strength | ASTM D4812 | 620 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| fracture | ASTM D638 | 141 MPa | |
| ISO 527-2/5 | 140 MPa | ||
| ASTM D638 | 2.3 % | ||
| ISO 527-2/5 | 2.2 % | ||
| ASTM D790 | 211 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 98.0 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.6E-05 cm/cm/°C | |
| ISO 11359-2 | 5.8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.