Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LNP™ THERMOCOMP™ D452 compound SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/LNP™ THERMOCOMP™ D452 compound |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 13 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 150 J/m |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 620 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 41 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC/LNP™ THERMOCOMP™ D452 compound |
|---|---|---|---|
| fracture | ASTM D638 | 2.3 % | |
| ISO 527-2/5 | 140 MPa | ||
| ASTM D638 | 141 MPa | ||
| ISO 527-2/5 | 2.2 % | ||
| ASTM D790 | 211 MPa |
| flammability | Test Condition | Test Method | SABIC/LNP™ THERMOCOMP™ D452 compound |
|---|---|---|---|
| UL flame retardant rating | 1.00mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC/LNP™ THERMOCOMP™ D452 compound |
|---|---|---|---|
| melt mass-flow rate | 300°C/2.16kg | ASTM D1238 | 39 g/10min |
| Shrinkage rate | TD:24小时 | ASTM D955 | 0.10to0.25 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 12.0 cm³/10min |
| density | ASTM D792 | 1.52 g/cm³ | |
| Shrinkage rate | MD:24小时 | ASTM D955 | 0.10to0.25 % |
| Melt volume flow rate | 300°C/2.16kg | ISO 1133 | 30.0 cm³/10min |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 17 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC/LNP™ THERMOCOMP™ D452 compound |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:23到80°C | ISO 11359-2 | 5.8E-05 cm/cm/°C |
| MD:23到80°C | ISO 11359-2 | 1.6E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 98.0 °C |