Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 22 g/10min |
| Water absorption rate | | ASTMD570 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 120 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTMD542 | 1.586 |
| transmissivity | | ASTMD1003 | 89.0 % |
| Haze ratio | | ASTMD1003 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-2 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 775 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 750 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD638 | 60.3 MPa |
| elongation | | ASTMD638 | 120 % |
| Flexural modulus | | ASTMD790 | 2410 MPa |
| bending strength | | ASTMD790 | 89.6 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Hot wire ignition (HWI) | | UL746 | PLC 3 |
| Hot wire ignition (HWI) | | UL746 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | 250到400 V |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 2 |
| High arc combustion index (HAI) | | UL746 | >120 |
| High arc combustion index (HAI) | | UL746 | 60.0到120 |
| High arc combustion index (HAI) | | UL746 | PLC 0 |
| High arc combustion index (HAI) | | UL746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | 80.0到150 mm/min |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 3 |
| Hot wire ignition (HWI) | | UL746 | 15到30 sec |
| Hot wire ignition (HWI) | | UL746 | 30到60 sec |
| arc resistance | | ASTMD495 | 60.0到120 sec |
| arc resistance | | ASTMD495 | PLC6 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | | ASTMD648 | 127 °C |
| Heat Deflection Temperature | | ISO75-2/A | 137 °C |
| Linear thermal expansion coefficient | | ASTME831 | 7E-05 cm/cm/°C |
| Linear thermal expansion coefficient | | ASTME831 | 6.8E-05 cm/cm/°C |
| RTI Elec | | UL746 | 125 °C |
| RTI Imp | | UL746 | 115 °C |
| RTI | | UL746 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare