Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D1505 | 0.948 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 0.24 g/10min |
| Environmental stress cracking resistance | | ASTM D1693 | >1000 hr |
| Carbon black content | | ASTM D4218 | 2.5 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 55 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ASTM D638 | 37.0 MPa |
| elongation | Break | ASTM D638 | 790 % |
| Flexural modulus | | ASTM D790 | 600 MPa |
| tensile strength | Yield | ASTM D638 | 24.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 98 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 20 kV/mm |
| dielectric constant | | ASTM D1531 | 2.50 |
| Dissipation Factor | | ASTM D1531 | 5E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | <-75.0 °C |
| Oxygen induction time | | ASTM D3895 | >100 min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.