POM Copolymer

POM Copolymer Ekatal® H 3 Sattler KunststoffWerk GmbH

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.4 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	2740 MPa
tensile strength	Yield	ISO 527-2	68.8 MPa
tensile strength	tensile strength	Break	ISO 527-2	64.0 MPa
Tensile strain	Yield	ISO 527-2	15 %
Tensile strain	Tensile strain	Break	ISO 527-2	42 %
Bending modulus		ISO 178	2700 MPa
bending strength	--	ISO 178	95.9 MPa
bending strength	bending strength	3.5%Strain	ISO 178	75.7 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	103 °C
Linear coefficient of thermal expansion	MD:20to52°C	ISO 11359-2	1.1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	MD:52to117°C	ISO 11359-2	1.3E-04 cm/cm/°C
		Linear coefficient of thermal expansion	TD:20to52°C	ISO 11359-2	9.9E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:52to117°C	ISO 11359-2	1.3E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.41 g/cm³
melt mass-flow rate	190°C/2.16kg	ISO 1133	3.0 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.