POM Copolymer Ekatal® H 3 Sattler KunststoffWerk GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Sattler KunststoffWerk GmbH/Ekatal® H 3 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
| -30°C | ISO 179/1eA | 9.4 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Sattler KunststoffWerk GmbH/Ekatal® H 3 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2740 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 64.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 42 % |
| bending strength | 3.5%应变 | ISO 178 | 75.7 MPa |
| Tensile strain | 屈服 | ISO 527-2 | 15 % |
| tensile strength | 屈服 | ISO 527-2 | 68.8 MPa |
| bending strength | -- | ISO 178 | 95.9 MPa |
| Flexural modulus | ISO 178 | 2700 MPa |
| physical property | Test Condition | Test Method | Sattler KunststoffWerk GmbH/Ekatal® H 3 |
|---|---|---|---|
| density | ISO 1183 | 1.41 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 3.0 g/10min |
| Thermal performance | Test Condition | Test Method | Sattler KunststoffWerk GmbH/Ekatal® H 3 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 103 °C |
| Linear coefficient of thermal expansion | MD:20到52°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| TD:52到117°C | ISO 11359-2 | 1.3E-04 cm/cm/°C | |
| TD:20到52°C | ISO 11359-2 | 9.9E-05 cm/cm/°C | |
| MD:52到117°C | ISO 11359-2 | 1.3E-04 cm/cm/°C |