ABS

ABS CYCOLAC™ MG47 BK1066 SABIC INNOVATIVE SINGAPHORE

Properties:
High glossHigh impact resistanceLow temperature resistancHigh toughness
Usages:
small home appliances
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	26 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	8.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	22 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	30.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Yield	ISO 527-2/50	2.6 %
elongation	Yield	ASTM D638	2.0 %
tensile strength	Break	ISO 527-2/50	35.0 Mpa
tensile strength	tensile strength	Yield	ASTM D638	44.0 Mpa
Tensile modulus		ISO 527-2/1	2370 Mpa
Tensile modulus	Tensile modulus		ASTM D638	2270 Mpa
elongation	Break	ASTM D638	24 %
Tensile strain	Break	ISO 527-2/50	25 %
Bending modulus	50.0mmSpan	ASTM D790	2300 Mpa
Bending modulus	Bending modulus		ISO 178	2200 Mpa
bending strength		ISO 178	70.0 Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	70.0 Mpa
tensile strength	Break	ASTM D638	33.0 Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	47.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Str		UL 746	60.0 °C
RTI Imp		UL 746	60.0 °C
RTI Elec		UL 746	60.0 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	8.8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	8.8E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	100 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	98.0 °C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	94.0 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	80.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	81.0 °C
Vicat softening temperature		ASTM D152510	99.0 °C

Physical properties	Test Condition	Test Method	Test Result
Melt viscosity	240°C,1000sec^-1	ASTM D3835	225 Pa·s
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.80 %
melt mass-flow rate	220°C/10.0kg	ISO 1133	18 g/10min
melt mass-flow rate	melt mass-flow rate	230°C/3.8kg	ASTM D1238	5.6 g/10min

Electrical performance	Test Condition	Test Method	Test Result
High arc combustion index	HAI	UL 746	PLC 0
Hot wire ignition	HWI	UL 746	PLC 3
High voltage arc tracing rate	HVTR	UL 746	PLC 3
Compared to the anti leakage trace index	CTI	UL 746	PLC 0
Arc resistance		ASTM D495	PLC6

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	112

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.