Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS MG47 BK1066 SABIC INNOVATIVE SINGAPHORE
CYCOLAC™
small home appliances
High gloss、High impact resistance、Low temperature resistanc、High toughness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/MG47 BK1066 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 8.0 kJ/m² |
| 23°C | ISO180/1A | 22 kJ/m² | |
| Impact strength of simply supported beam gap 7 | -30°C | ISO179/1eA | 9.0 kJ/m² |
| 23°C | ISO179/1eA | 26 kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 30.0 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/MG47 BK1066 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTMD785 | 112 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/MG47 BK1066 |
|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2/50 | 47.0 Mpa |
| elongation | 断裂 | ASTMD638 | 24 % |
| Bending strength 5,6 | ISO178 | 70.0 Mpa | |
| Tensile modulus | ASTMD638 | 2270 Mpa | |
| Tensile strain | 屈服 | ISO527-2/50 | 2.6 % |
| Tensile stress | 断裂 | ISO527-2/50 | 35.0 Mpa |
| elongation | 屈服 | ASTMD638 | 2.0 % |
| Tensile modulus | ISO527-2/1 | 2370 Mpa | |
| tensile strength | 屈服 | ASTMD638 | 44.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTMD790 | 70.0 Mpa |
| tensile strength | 断裂 | ASTMD638 | 33.0 Mpa |
| Tensile strain | 断裂 | ISO527-2/50 | 25 % |
| Flexural modulus | ISO178 | 2200 Mpa | |
| 50.0mm跨距 | ASTMD790 | 2300 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/MG47 BK1066 |
|---|---|---|---|
| High arc combustion index (HAI) | HAI | UL746 | PLC 0 |
| Arc resistance 11 | ASTMD495 | PLC6 | |
| Hot wire ignition (HWI) | HWI | UL746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL746 | PLC 3 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL746 | PLC 0 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/MG47 BK1066 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/MG47 BK1066 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.80 % |
| melt mass-flow rate | 220°C/10.0kg | ISO1133 | 18 g/10min |
| melt viscosity | 240°C,1000sec^-1 | ASTMD3835 | 225 Pa·s |
| melt mass-flow rate | 230°C/3.8kg | ASTMD1238 | 5.6 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/MG47 BK1066 |
|---|---|---|---|
| 1.8MPa,未退火,3.20mm | ASTMD648 | 80.0 °C | |
| RTI Str | UL746 | 60.0 °C | |
| MD：-40到40°C | ASTME831 | 8.8E-05 cm/cm/°C | |
| RTI Elec | UL746 | 60.0 °C | |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 94.0 °C | |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 81.0 °C |
| vicat | -- | ISO306/B50 | 98.0 °C |
| -- | ISO306/B120 | 100 °C | |
| RTI Imp | UL746 | 60.0 °C | |
| TD：-40到40°C | ASTME831 | 8.8E-05 cm/cm/°C | |
| vicat | ASTMD152510 | 99.0 °C |