ABS/PC CYCOLAC™ DL200H-BK4051 SABIC INNOVATIVE NANSHA
666
- Properties:High heat resistanceHydrolysis resistance
- Usages:Automotive componentsElectronic and electrical
Compare
View PricesTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 熔体质量流动速率 | 260°C/5.0kg | ASTMD1238 | 25 g/10min |
| 220°C/10.0kg | ISO1133 | 9.0 g/10min |
| 热性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 热变形温度 | 0.45MPa,未退火,3.20mm | ASTMD648 | 118 °C |
| 热变形温度9 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 120 °C |
| 热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 96.0 °C |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 101 °C | |
| 热变形温度9 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 96.0 °C |
| 维卡软化温度 | -- | ISO306/B50 | 112 °C |
| -- | ISO306/B120 | 114 °C |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 拉伸模量 | ASTMD638 | 2330 Mpa | |
| ISO527-2/1 | 2350 Mpa | ||
| 抗张强度 | 屈服 | ASTMD638 | 47.0 Mpa |
| 拉伸应力 | 屈服 | ISO527-2/50 | 49.0 Mpa |
| 断裂 | ISO527-2/50 | 40.0 Mpa | |
| 拉伸应变 | 屈服 | ISO527-2/50 | 3.9 % |
| 伸长率 | 断裂 | ASTMD638 | 70 % |
| 拉伸应变 | 断裂 | ISO527-2/50 | 75 % |
| 弯曲模量 | 50.0mm跨距 | ASTMD790 | 2200 Mpa |
| ISO178 | 2100 Mpa | ||
| 弯曲强度5,6 | ISO178 | 75.0 Mpa | |
| 弯曲强度 | 屈服,50.0mm跨距 | ASTMD790 | 77.0 Mpa |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | 23°C | ISO180/1A | 56 kJ/m² |
| 简支梁缺口冲击强度7 | -30°C | ISO179/1eA | 30 kJ/m² |
| 23°C | ISO179/1eA | 65 kJ/m² | |
| 悬壁梁缺口冲击强度 | -40°C | ISO180/1A | 21 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.