Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS/PC DL200H-BK4051 SABIC INNOVATIVE NANSHA
CYCOLAC™
Automotive components、Electronic and electrical
High heat resistance、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DL200H-BK4051 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 101 °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 96.0 °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 112 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 118 °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 120 °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 96.0 °C | |
| Vicat Softening Temperature | -- | ISO306/B120 | 114 °C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DL200H-BK4051 |
|---|---|---|---|
| Melt Mass-Flow Rate | 220°C/10.0kg | ISO1133 | 9.0 g/10min |
| 260°C/5.0kg | ASTMD1238 | 25 g/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DL200H-BK4051 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2200 Mpa |
| ISO178 | 2100 Mpa | ||
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 77.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 40.0 Mpa |
| 屈服 | ISO527-2/50 | 49.0 Mpa | |
| Tensile Elongation | 断裂 | ASTMD638 | 70 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 75 % |
| 屈服 | ISO527-2/50 | 3.9 % | |
| Tensile Modulus | ISO527-2/1 | 2350 Mpa | |
| Flexural Strength | ISO178 | 75.0 Mpa | |
| Tensile Modulus | ASTMD638 | 2330 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 47.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DL200H-BK4051 |
|---|---|---|---|
| Notched Izod Impact Strength | -40°C | ISO180/1A | 21 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 30 kJ/m² |
| 23°C | ISO179/1eA | 65 kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 56 kJ/m² |