Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | Equilibrium | ASTMD570 | 0.78 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 81 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTMD638 | 11到25 % |
| Flexural modulus | | ASTMD790 | 1190到1380 MPa |
| bending strength | | ASTMD790 | 40.0到45.0 MPa |
| Tensile modulus | | ASTMD638 | 1250到1510 MPa |
| tensile strength | | ASTMD638 | 31.0到39.0 MPa |
| elongation | Yield | ASTMD638 | 16 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256A | 27到50 J/m |
| film | Test Condition | Test Method | Test Result |
|---|
| GravesTear | | ASTMD1004 | 154.3 kN/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTME381 | 1.7E-4到1.9E-4 cm/cm/°C |
| | ASTME381 | 1.9E-4到2.0E-4 cm/cm/°C |
| Heat distortion temperature | | ASTMD648 | 84.5到103 °C |
| Heat distortion temperature | | ASTMD648 | 65.4到88.0 °C |
| Glass Transition Temperature | | ASTME1545 | 37.0到52.0 °C |
| | ASTME381 | 5.5E-5到6.3E-5 cm/cm/°C |
| | ASTME381 | 8.8E-5到9.4E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.