PA6 Ultramid® B3EG3 BK00564
59
- Properties:Oil resistantHigh impact resistanceFiller: Glass fiber reinf15% filler by weight15% filler by weight
- Usages:Automotive sectorwheelShellApplication in the automotive fieldwheelShell
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.23 g/cm³ | |
| Water absorption rate | ISO 62 | 7.7 % | |
| ISO 62 | 2.3 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 6060 Mpa | |
| tensile strength | ISO 527-2 | 115 Mpa | |
| Tensile strain | ISO 527-2 | 2.5 % | |
| Flexural modulus | ISO 178 | 5300 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 5.0 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180 | 4.5 kJ/m² | |
| ISO 180 | 5.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| dielectric constant | IEC 60250 | 3.80 | |
| Dissipation Factor | IEC 60250 | 0.025 | |
| IEC 60250 | 0.025 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 217 °C | |
| ISO 75-2/A | 200 °C | ||
| melting temperature | ISO 3146 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.