PA6 B3EG3 BK00564 BASF SHANGHAI
Ultramid®
Automotive sector、wheel、Shell、Application in the automo、wheel、Shell
Oil resistant、High impact resistance、Filler: Glass fiber reinf、15% filler by weight、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | BASF SHANGHAI/B3EG3 BK00564 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 5.0 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180 | 5.0 kJ/m² |
-30°C | ISO 180 | 4.5 kJ/m² |
Electrical performance | Test Condition | Test Method | BASF SHANGHAI/B3EG3 BK00564 |
---|---|---|---|
Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
Dissipation Factor | 100Hz | IEC 60250 | 0.025 |
dielectric constant | 1MHz | IEC 60250 | 3.80 |
Dissipation Factor | 1MHz | IEC 60250 | 0.025 |
Mechanical properties | Test Condition | Test Method | BASF SHANGHAI/B3EG3 BK00564 |
---|---|---|---|
Tensile strain | 断裂,23°C | ISO 527-2 | 2.5 % |
Flexural modulus | 23°C | ISO 178 | 5300 Mpa |
Tensile modulus | 23°C | ISO 527-2 | 6060 Mpa |
tensile strength | 断裂,23°C | ISO 527-2 | 115 Mpa |
physical property | Test Condition | Test Method | BASF SHANGHAI/B3EG3 BK00564 |
---|---|---|---|
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.3 % |
饱和,23°C | ISO 62 | 7.7 % | |
density | ISO 1183 | 1.23 g/cm³ |
Thermal performance | Test Condition | Test Method | BASF SHANGHAI/B3EG3 BK00564 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 217 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 200 °C | |
melting temperature | ISO 3146 | 220 °C |