ABS Esterlloy™ AT900
31
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 12 g/10 min | |
| Melt volume flow rate | ISO 1133 | 13.0 cm3/10min | |
| melt mass-flow rate | ISO 1133 | 12 g/10min | |
| Melt volume flow rate | ISO 1133 | 12.5 cm3/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | 118 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | 118 R 计秤 | ||
| tensile strength | ISO 527-2/5 | 64.0 Mpa | |
| Flexural modulus | ISO 178 | 2950 Mpa | |
| bending strength | ISO 178 | 99.0 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 3.0 kJ/m² | |
| tensile strength | ISO 527-2/50 | 64.1 Mpa | |
| Flexural modulus | ISO 178 | 2950 Mpa | |
| bending strength | ISO 178 | 98.6 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.14 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 81.0 °C | |
| vicat | ISO 306/B | 104 °C | |
| Heat distortion temperature | ISO 75-2/A | 80.9 °C | |
| vicat | ISO 306/B | 104 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.