Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS AT900 ASAHI JAPAN
Esterlloy™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | ASAHI JAPAN/AT900 |
|---|---|---|---|
| Rockwell hardness | R计秤,2.50mm | 118 |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/AT900 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 64.0 Mpa |
| 屈服 | ISO 527-2/50 | 64.1 Mpa | |
| Rockwell hardness | 2.50 mm | 118 R 计秤 | |
| bending strength | ISO 178 | 98.6 Mpa | |
| Flexural modulus | ISO 178 | 2950 Mpa | |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 3.0 kJ/m² |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/AT900 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.14 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 12 g/10min |
| physical property | Test Condition | Test Method | ASAHI JAPAN/AT900 |
|---|---|---|---|
| Melt volume flow rate | 220℃/10.0 kg | ISO 1133 | 13.0 cm3/10min |
| melt mass-flow rate | 220℃/10.0 kg | ISO 1133 | 12 g/10 min |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 12.5 cm3/10min |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/AT900 |
|---|---|---|---|
| vicat | ISO 306/B | 104 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 81.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 80.9 °C |