Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 0.25 g/10 min |
| Environmental stress cracking resistance | | | 15.0 hr |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D2457 | > 35 |
| gloss | | ASTM D2457 | > 90 |
| Haze ratio | | ASTM D1003 | < 7.0 % |
| Failure Energy - Blown Film | | DIN 53373 | 50.0 J/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 300 Mpa |
| tensile strength | | ISO 527-2 | 13.0 Mpa |
| coefficient of friction | | ISO 8295 | > 0.70 |
| squeeze out | Test Condition | Test Method | Test Result |
|---|
| Melt Temperature | | | 170 to 220 °C |
| film | Test Condition | Test Method | Test Result |
|---|
| Film thickness - tested | | | 50 µm |
| tensile strength | | ISO 527-3 | 30.0 Mpa |
| tensile strength | | ISO 527-3 | 27.0 Mpa |
| elongation | | ISO 527-3 | 250 % |
| elongation | | ISO 527-3 | 600 % |
| Dart impact | | ASTM D1709 | 180 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/A50 | 102 °C |
| melting temperature | | ISO 3146 | 114 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.