LDPE 3010D LYONDELLBASELL HOLAND
LUPOLEN
film、Bag
Processability、High toughness、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | LYONDELLBASELL HOLAND/3010D |
|---|---|---|---|
| elongation | TD : 断裂, 50 µm, 吹塑薄膜 | ISO 527-3 | 600 % |
| tensile strength | MD : 50 µm, 吹塑薄膜 | ISO 527-3 | 30.0 Mpa |
| TD : 50 µm, 吹塑薄膜 | ISO 527-3 | 27.0 Mpa | |
| Film thickness - tested | 50 µm | ||
| elongation | MD : 断裂, 50 µm, 吹塑薄膜 | ISO 527-3 | 250 % |
| Dart impact | 50 µm, 吹塑薄膜 | ASTM D1709 | 180 g |
| Mechanical properties | Test Condition | Test Method | LYONDELLBASELL HOLAND/3010D |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 300 Mpa | |
| coefficient of friction | 吹塑薄膜 | ISO 8295 | > 0.70 |
| tensile strength | 屈服 | ISO 527-2 | 13.0 Mpa |
| optical performance | Test Condition | Test Method | LYONDELLBASELL HOLAND/3010D |
|---|---|---|---|
| gloss | 60°, 50.0 µm, 吹塑薄膜 | ASTM D2457 | > 90 |
| Failure Energy - Blown Film | 50.0 µm | DIN 53373 | 50.0 J/cm |
| Haze ratio | 50.0 µm, 吹塑薄膜 | ASTM D1003 | < 7.0 % |
| gloss | 20°, 50.0 µm, 吹塑薄膜 | ASTM D2457 | > 35 |
| squeeze out | Test Condition | Test Method | LYONDELLBASELL HOLAND/3010D |
|---|---|---|---|
| Melt Temperature | 170 to 220 °C |
| physical property | Test Condition | Test Method | LYONDELLBASELL HOLAND/3010D |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16 kg | ISO 1133 | 0.25 g/10 min |
| Environmental stress cracking resistance | 条件 B, 10% Igepal, F10 | 15.0 hr |
| Thermal performance | Test Condition | Test Method | LYONDELLBASELL HOLAND/3010D |
|---|---|---|---|
| vicat | ISO 306/A50 | 102 °C | |
| melting temperature | ISO 3146 | 114 °C |