| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 2577 | 1.0 - 1.2 % |
| Shrinkage rate | | ISO 2577 | 1.0 - 1.2 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS 302 | < 100 mm/min |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 750 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 3600 Mpa |
| tensile strength | | ISO 527-2/50 | 80.0 Mpa |
| Tensile strain | | ISO 527-2/50 | 15 % |
| Flexural modulus | | ISO 178 | 3300 Mpa |
| bending strength | | ISO 178 | 120 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 80 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 70 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1.0E+13 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 75 to 85 °C |
| drying time | | | 2.0 to 4.0 hr |
| Processing (melt) temperature | | | 260 to 280 °C |
| Temperature | | | 60 to 80 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 200 °C |
| Heat distortion temperature | | ISO 75-2/A | 75.0 °C |
| vicat | | ISO 306/B50 | 215 °C |
| melting temperature | | ISO 11357-3 | 262 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.