Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO1133 | 2.00 cm3/10min |
| Shrinkage rate | | ISO294-4 | 0.60到0.80 % |
| Dissolved volume flow rate | | ISO 1133 | 2.00 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 0.60 到 0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 100 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 2150 Mpa |
| Tensile stress | | ISO527-2 | 40.0 Mpa |
| Bending modulus 2 | | ISO178 | 2230 Mpa |
| Bending stress 2 | | ISO178 | 65.0 Mpa |
| Tensile stress | | ISO 527-2 | 40.0 Mpa |
| Flexural modulus | | ISO 178 | 2230 Mpa |
| bending strength | | ISO 178 | 65.0 Mpa |
| Charpy Notched Impact Strength | | ISO 179 | 3.0 kJ/m² |
| Rockwell hardness | | ISO 2039-2 | 100 R 计秤 |
| Tensile modulus | | ISO 527-2 | 2150 Mpa |
| Izod notch impact strength | | ASTM D256/ISO 179 | 3 kg·cm/cm(J/M)ft·lb/in |
| Tensile modulus | | ASTM D638/ISO 527 | 2150 kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ASTM D638/ISO 527 | 40 kg/cm²(MPa)[Lb/in²] |
| Rockwell hardness | | ASTM D785 | 100 |
| Flexural modulus | | ASTM D790/ISO 178 | 2230 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 65 kg/cm²(MPa)[Lb/in²] |
| Izod notch impact strength | | ASTM D256/ISO 179 | 6 kg·cm/cm(J/M)ft·lb/in |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.21 |
| Mold Shrinkage | | ASTM D955 | 0.6~0.8 % |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 2 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/Af | 105 °C |
| | ISO11359-2 | 8E-05 cm/cm/°C |
| | ISO 75-2/Af | 105 °C |
| Linear expansion coefficient | | ISO 11359-2 | 0.000080 cm/cm/℃ |
| UL flame retardant rating | | UL 94 | V-0 |
| Combustibility (rate) | | UL94 | 1.5 V-0 |
| | ASTM D648/ISO 75 | 105 ℃（℉） |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 8 mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare