Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS NTV35 UMG JAPAN
UMG ABS®
--
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UMG JAPAN/NTV35 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO2039-2 | 100 |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/NTV35 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 65 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2230 kg/cm²(MPa)[Lb/in²] | |
| Izod notch impact strength | ASTM D256/ISO 179 | 6 kg·cm/cm(J/M)ft·lb/in | |
| Flexural modulus | 23℃ | ISO 178 | 2230 Mpa |
| Bending modulus 2 | 23°C | ISO178 | 2230 Mpa |
| Tensile stress | 23℃ | ISO 527-2 | 40.0 Mpa |
| Rockwell hardness | 23℃ | ISO 2039-2 | 100 R 计秤 |
| Tensile stress | 23°C | ISO527-2 | 40.0 Mpa |
| Rockwell hardness | ASTM D785 | 100 | |
| Tensile modulus | 23℃ | ISO 527-2 | 2150 Mpa |
| tensile strength | ASTM D638/ISO 527 | 40 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | 23°C | ISO527-2 | 2150 Mpa |
| Charpy Notched Impact Strength | -30℃ | ISO 179 | 3.0 kJ/m² |
| Bending stress 2 | 23°C | ISO178 | 65.0 Mpa |
| Tensile modulus | ASTM D638/ISO 527 | 2150 kg/cm²(MPa)[Lb/in²] | |
| bending strength | 23℃ | ISO 178 | 65.0 Mpa |
| Physical properties | Test Condition | Test Method | UMG JAPAN/NTV35 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.21 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 2 g/10min | |
| Mold Shrinkage | ASTM D955 | 0.6~0.8 % |
| flammability | Test Condition | Test Method | UMG JAPAN/NTV35 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 |
| physical property | Test Condition | Test Method | UMG JAPAN/NTV35 |
|---|---|---|---|
| Shrinkage rate | MD，23℃ | ISO 294-4 | 0.60 到 0.80 % |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 2.00 cm3/10min |
| Shrinkage rate | MD：23°C | ISO294-4 | 0.60到0.80 % |
| Dissolved volume flow rate | 220℃/2.16 kg | ISO 1133 | 2.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/NTV35 |
|---|---|---|---|
| 1.8MPa,未退火 | ISO75-2/Af | 105 °C | |
| Linear expansion coefficient | 流动 | ISO 11359-2 | 0.000080 cm/cm/℃ |
| ASTM D648/ISO 75 | 105 ℃（℉） | ||
| 1.80MPa，未退火 | ISO 75-2/Af | 105 °C | |
| MD | ISO11359-2 | 8E-05 cm/cm/°C | |
| Combustibility (rate) | UL94 | 1.5 V-0 | |
| UL flame retardant rating | UL 94 | V-0 | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 8 mm/mm.℃ |