PEI+PCE ULTEM™ AUT195 resin

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ASTM D792	1.26 g/cm³
density	density		ISO 1183	1.27 g/cm³
melt mass-flow rate		ASTM D1238	24 g/10min
Melt volume flow rate		ISO 1133	16.0 cm³/10min
Shrinkage rate		内部方法	0.50to0.70 %
Shrinkage rate	Shrinkage rate		内部方法	0.50to0.70 %
Water absorption rate		ISO 62	0.90 %
Water absorption rate	Water absorption rate		ISO 62	0.50 %

Supplementary Information	Test Condition	Test Method	Test Result
Metallic haze		内部方法	195 °C

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256	53 J/m
	Impact strength of cantilever beam gap		ISO 180/1A	5.0 kJ/m²
		Impact strength of cantilever beam gap		ISO 180/1A	5.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D4812	2100 J/m
Charpy Notched Impact Strength		ISO 179/1eA	4.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	4.0 kJ/m²
Impact strength of cantilever beam gap		ASTM D256	2100 J/m

Mechanical properties	Test Condition	Test Method	Test Result
elongation	Break	ASTM D638	70 %
Flexural modulus		ASTM D790	3170 MPa
Flexural modulus	Flexural modulus		ISO 178	3100 MPa
bending strength		ASTM D790	145 MPa
Tensile modulus		ISO 527-2/1	3000 MPa
tensile strength	Yield	ASTM D638	96.5 MPa

Thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion		ISO 11359-2	6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	6E-05 cm/cm/°C
thermal conductivity		ISO 8302	0.23 W/m/K
Heat distortion temperature		ISO 75-2/Be	195 °C
	Heat distortion temperature		ASTM D648	190 °C
	Heat distortion temperature	Heat distortion temperature		ISO 75-2/Ae	180 °C
vicat		ISO 306/B120	205 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.