Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI+PCE ULTEM™ AUT195 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/ULTEM™ AUT195 resin |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 53 J/m |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
| 23°C | ASTM D4812 | 2100 J/m | |
| 23°C | ISO 180/1A | 5.0 kJ/m² | |
| 3.20mm | ASTM D256 | 2100 J/m |
| Supplementary Information | Test Condition | Test Method | SABIC/ULTEM™ AUT195 resin |
|---|---|---|---|
| Metallic haze | 起始 | 内部方法 | 195 °C |
| Mechanical properties | Test Condition | Test Method | SABIC/ULTEM™ AUT195 resin |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 70 % |
| bending strength | Yield,100mmSpan | ASTM D790 | 145 MPa |
| tensile strength | 屈服 | ASTM D638 | 96.5 MPa |
| Flexural modulus | 100mmSpan | ASTM D790 | 3170 MPa |
| ISO 178 | 3100 MPa | ||
| Tensile modulus | ISO 527-2/1 | 3000 MPa |
| physical property | Test Condition | Test Method | SABIC/ULTEM™ AUT195 resin |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| TD2 | 内部方法 | 0.50to0.70 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.50 % |
| Melt volume flow rate | 340°C/5.0kg | ISO 1133 | 16.0 cm³/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.90 % |
| density | ASTM D792 | 1.26 g/cm³ | |
| ISO 1183 | 1.27 g/cm³ | ||
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 24 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC/ULTEM™ AUT195 resin |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Be | 195 °C |
| thermal conductivity | ISO 8302 | 0.23 W/m/K | |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 190 °C |
| Linear coefficient of thermal expansion | TD：23to150°C | ISO 11359-2 | 6E-05 cm/cm/°C |
| vicat | ISO 306/B120 | 205 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 180 °C |
| Linear coefficient of thermal expansion | MD：23到150°C | ISO 11359-2 | 6E-05 cm/cm/°C |