ABS Terluran® GP-25 INEOS STYRO KOREA

Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Huangdu Index		DIN 6167	15 YI

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield,23°C	ISO 527-2	44 Mpa
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	22 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	90 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	125 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	7 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	19 kJ/m²
Tensile modulus	23°C	ISO 527-2	2300 Mpa
Elongation at Break	23°C	ISO 527-2	12 %
Elongation at Break	Elongation at Break	Yield,23°C	ISO 527-2	2.4 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.80MPaUnannealed	ISO 75-2/Af	93 °C
Vicat softening temperature	5.1kg	ISO 306/A50	95 °C
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	97 °C
thermal conductivity		DIN 52612	0.170 W/m/K
Linear coefficient of thermal expansion	MD	ISO 11359-2	8.0E-5 cm/cm/°C
Melting temperature		ISO 11357-3	220-260 °C
Vicat softening temperature	1.02kg	ISO 306/B50	103 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD2.0mm	ISO 294-4	0.4 %
Shrinkage rate	Shrinkage rate	TD2.0mm	ISO 294-4	0.7 %
Water absorption rate	23°C,24hr	ISO 62	0.21 %
Water absorption rate	Water absorption rate	23°C,50RH	ISO 62	0.95 %
melt mass-flow rate	220℃/10Kg	ISO 1133	25 g/10min

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	>=1.0E+15 Ω.cm

flame retardancy	Test Condition	Test Method	Test Result
UL flame retardant rating	Allcolor	UL -94	HB 3.00mm
UL flame retardant rating	UL flame retardant rating	Allcolor	UL -94	HB 1.50mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.